IBC Coatings Technologies manufactures a wide range of standard and custom locator and welding pins. IBC’s locator pins have been tailored for maximum performance using a combination of high strength materials and state-of-the-art surface treatments. IBC’s locator pins are providing industry leading durability and life making them a preferred choice for automotive OEMs and integrators. IBC specializes in providing high quality custom pins with fast turnaround to meet the demands of the automotive industry. Customers using IBC locator pins have reported over 10x life improvement resulting in lower operating cost and reduced downtime.

General Information:

Locator pins are used for precise positioning of components during joining and assembly. The joining can be performed using several techniques including brazing, welding, riveting, gluing, and fastening. As the locator pins repeatedly come into contact with components during the position alignment, they experience considerable wear and impact, hence they should be manufactured with high tolerances from durable materials that can withstand high wear and impact.

NAAMS Global Standard Components defines approved components utilized in the design and manufacturing of tooling to produce various sheet metal products, as part of the vehicle body assembly production process. This includes locator pins, for which standards are described in the NAAMS classification.

Locator pins used in welding assemblies require additional mechanical and functional properties such as resistance to welding splatter, as well as being electrically insulating. Welding pins are used in Nut welding, specifically as part of the process that is aimed on positioning of the nut.

In Projection welding, the weld is localized by means of raised sections or projections, on one or both workpieces to be joined. The projections can also serve as a means of positioning the workpieces. Projection welding is often used to weld studs, nuts, and other screw machine parts to a metal plate. Projection welding equipment is the biggest consumer of welding pins. Additionally, welding pins need to be electrically insulating.

Challenges to the locator and welding pins in modern manufacturing environment:

A common trend in manufacturing today is that the majority of manufacturers are striving to reduce the weight of their equipment to minimize fuel consumption. This requires new materials that are lighter and stronger, and new processes that can handle these changes. Examples of new materials include high strength steel, aluminum, and titanium alloys; and examples of new processes include hot forming and laser cutting. Traditional locator and welding pins do not provide enough longevity in the new environment and require frequent replacements.

IBC’s solution for locator and welding pins:

IBC Coatings Technologies has applied the principles of material engineering to solve the shortcomings of existing locator and welding pin designs. Starting from the selection of materials – IBC’s pins are manufactured from high strength/high toughness tool steels capable of working at high temperatures. IBC has developed and applied diffusion based coating systems, for both its locator and welding pins, that provide high hardness, low coefficient of friction, electrical insulation, and weld splatter resistance.

IBC developed two types of pins to meet the needs of today’s manufacturers:

  1. CeraTough™-D specifically designed for locator and welding pins that require electrical insulation and weld splatter resistance.
  2. CeraTough™-D Rainbow for locator pins that do not require electrical insulation and welding splatter resistance.

IBC is equipped with the state-of-the-art tribological testing capabilities. This includes on-site equipment such as the latest wear tester (Bruker UMT TriboLab) and profilometer (ContourG-TK 3D). Using this equipment, Wear Testing per ASTM G133 (Linearly Reciprocating Ball-on-Flat), Metallurgical, and 3D Non-Contact Profilometry Analyses were performed to select the best material/coating composition for the locator and welding pins. Wear testing provided coefficient of friction, as well as wear rates of surfaces for both types of IBC pins.

The standard unlubricated testing parameters per the ASTM G133 specification were as follows:

  • Ball Diameter: 3/8 in.
  • Normal Force: 25 N
  • Stroke Length: 10 mm
  • Frequency: 5 Hz
  • Time: 1000 sec (sliding distance of 100 m)
  • Temperature: 22+/-3 ℃
  • Relative Humidity: 40-60%

Metallurgical surface and cross-sectional analysis provided hardness and elastic modulus for the base materials and coatings, as well as coating thickness. 3D Non-Contact Profilometry provided surface roughness and a topographical map of the worn areas that was used to measure wear rate and performance.

The tool steels used for CeraTough™ pins include H13 and M2, among others. The analysis below shows the comparison of uncoated hardened M2 pin against 52100 steel with CeraTough™-D and CeraTough™-D Rainbow coatings.

Wear testing of Hardened M2 pin against 52100 steel
CoF (52100 Steel) 0.45
Wear Rate (mm3/Nm) 41.5x10-8
Hardness (HV) 700-800
Elastic Modulus (GPa) 200
Figure 1. Wear testing of Hardened M2 pin against 52100 steel.
100x Optical image of the wear zone with severe galling (Hardened M2 pin)
100x Optical image of the wear zone with severe galling (Hardened M2 pin)

The same test was repeated using samples of CeraTough-D™ and CeraTough-D™ Rainbow, the results are shown below for comparison:

CeraTough™-D

CeraToughTM-D coated M2 pin
CoF (52100 Steel) 0.05
Wear Rate (mm3/Nm) 20.2x10-8
Hardness (HV) 1100-1300
Elastic Modulus (GPa) 70
Coating Thickness (um) 15-20
Wear testing of CeraToughTM-D coated M2 pin against 52100 steel
500x optical image of the wear zone shows no galling
Figure 2. Wear testing of CeraToughTM-D coated M2 pin against 52100 steel. 500x optical image of the wear zone shows no galling.

CeraTough™-D Rainbow

CeraToughTM-D Rainbow coated M2 pin
CoF (52100 Steel) 0.05
Wear Rate (mm3/Nm) 6.82x10-8
Hardness (HV) 5000
Elastic Modulus (GPa) 175
Coating Thickness (um) 0.5
Wear testing of CeraToughTM-D Rainbow coated M2 pin against 52100 steel
500x optical image of the wear zone shows no galling
Figure 3. Wear testing of CeraToughTM–D Rainbow coated M2 pin against 52100 steel. 500x optical image of the wear zone shows no galling.

The chart below presents a comparison of different coatings for locator pins along with their respective hardness, wear rate, and relative life:

Comparison of different coatings for locator pins along with their respective hardness, wear rate, and relative life
In the charts above the subscript 001 through 003 indicates process variants.

CeraTough™-D coating is also electrically insulating, which leads to better welds when the locator pins are used in resistance welding assembly operations. Depending on the pin application, the electrical resistance of CeraTough™-D for wet / aqueous immersion applications can be tailored from 0.02 Ω – 195 MΩ (dry electrical resistances are higher), while CeraTough-D™ Rainbow operates best in low to moderate electrical potential environments, or where only intermittent contact is expected (direct grounding not likely) or is otherwise insulated.

CeraTough™ coatings have outstanding corrosion resistance characteristics. CeraTough™-D, tested in accordance with ASTM G85 Annex 4 (5% salt spray plus SO2 gas) can withstand up to 400 hours of exposure, or 1000+ hours of ASTM B117.

CeraTough™ Locator and Welding pin properties:

Property CeraTough™–D CeraTough™–D Rainbow
High hardness 1100-1300 HV 5000-7000 HV
Low coefficient of friction 0.05 0.05
High wear resistance Yes Yes
Electrical insulation Up to 195 MΩ No
Weld splatter resistant Yes No
Working temperature Up to 1100°F Up to 1100°F

Conclusions:

IBC offers two types of pins:

  1. CeraTough™-D for locator and welding pins that require electrical insulation and weld splutter resistance. (Drawing 9-12)
  2. CeraTough™-D Rainbow for locator pins that do not require electrical insulation and welding splutter resistance. (Drawing 5-8)

CeraTough™ Locator and welding pins are manufactured per NAAMAS standards, and per individual customer drawings.

CeraTough™ locating pins are in use across the world by major automobile manufacturers, where they have reliably demonstrated a life improvement of up to 14 times that of the replaced locating and welding pins in extreme applications.

CeraTough™ locating and welding pins’ performance is superior to the best on the market and comparable to ceramic pins but without the inherited brittleness of ceramic.

IBC Coatings Technologies

902 Hendricks Dr.
Lebanon, IN 46052
Tel. +1 (765) 482-9802
Fax +1 (765) 482-9805
E-mail info@ibccoatings.com

CeraTough™ Locator and Welding Pins Brochure